API RP 939-C
Guidelines for Avoiding Sulfidation (Sulfidic) Corrosion Failures in Oil Refineries - FIRST EDITION
Organization:
API - American Petroleum Institute
Year: 2009
Abstract: This recommended practice (RP) is applicable to hydrocarbon process streams containing sulfur compounds, with and without the presence of hydrogen, which operate at temperatures above approximately 450 °F (230 °C) up to about 1000 °F (540 °C). A threshold limit for sulfur content is not provided because within the past decade significant corrosion has occurred in the reboiler/fractionator sections of some hydroprocessing units at sulfur or H2S levels as low as 1 ppm. Nickel base alloy corrosion is excluded from the scope of this document.
While sulfidation can be a problem in some sulfur recovery units, sulfur plant combustion sections and external corrosion of heater tubes due to firing sulfur containing fuels in heaters are specifically excluded from the scope of this document.
While sulfidation can be a problem in some sulfur recovery units, sulfur plant combustion sections and external corrosion of heater tubes due to firing sulfur containing fuels in heaters are specifically excluded from the scope of this document.
Collections
:
Show full item record
| contributor author | API - American Petroleum Institute | |
| date accessioned | 2017-09-04T17:18:14Z | |
| date available | 2017-09-04T17:18:14Z | |
| date copyright | 05/01/2009 | |
| date issued | 2009 | |
| identifier other | ZKICMCAAAAAAAAAA.pdf | |
| identifier uri | https://yse.yabesh.ir/std/handle/yse/141570 | |
| description abstract | This recommended practice (RP) is applicable to hydrocarbon process streams containing sulfur compounds, with and without the presence of hydrogen, which operate at temperatures above approximately 450 °F (230 °C) up to about 1000 °F (540 °C). A threshold limit for sulfur content is not provided because within the past decade significant corrosion has occurred in the reboiler/fractionator sections of some hydroprocessing units at sulfur or H2S levels as low as 1 ppm. Nickel base alloy corrosion is excluded from the scope of this document. While sulfidation can be a problem in some sulfur recovery units, sulfur plant combustion sections and external corrosion of heater tubes due to firing sulfur containing fuels in heaters are specifically excluded from the scope of this document. | |
| language | English | |
| title | API RP 939-C | num |
| title | Guidelines for Avoiding Sulfidation (Sulfidic) Corrosion Failures in Oil Refineries - FIRST EDITION | en |
| type | standard | |
| page | 50 | |
| status | Active | |
| tree | API - American Petroleum Institute:;2009 | |
| contenttype | fulltext |