Standard Test Method for  Analysis of Aluminum and Aluminum Alloys by Spark Atomic Emission  Spectrometry

ASTM - ASTM International

ASTM E1251-24

Organization:

Year: 2024

Abstract: 5.1 The metallurgical properties of aluminum and its alloys are highly dependent on chemical composition. Precise and accurate analyses are essential to obtaining desired properties, meeting customer specifications, and minimizing scrap due to off-grade material. 5.2 This test method is applicable to chill cast specimens as defined in Practices E716 and can also be applied to other types of samples provided that suitable reference materials are available. Also, other sample forms can be melted and cast into a disk, using an appropriate mold, as described in Practices E716. However, some elements (for example, magnesium) readily form oxides, while others (for example, sodium, lithium, calcium, and strontium) are volatile, and may be lost to varying degrees during the melting process.

URI: https://yse.yabesh.ir/std/handle/yse/341236

Collections :

ASTM - ASTM International

Download PDF : (309.2Kb)
Show Full MetaData Hide Full MetaData
Statistics

Standard Test Method for Analysis of Aluminum and Aluminum Alloys by Spark Atomic Emission Spectrometry

Show full item record

contributor author	ASTM - ASTM International
date accessioned	2025-09-30T18:00:37Z
date available	2025-09-30T18:00:37Z
date copyright	2024
date issued	2024
identifier other	e1251-24.pdf
identifier uri	https://yse.yabesh.ir/std/handle/yse/341236
description abstract	5.1 The metallurgical properties of aluminum and its alloys are highly dependent on chemical composition. Precise and accurate analyses are essential to obtaining desired properties, meeting customer specifications, and minimizing scrap due to off-grade material. 5.2 This test method is applicable to chill cast specimens as defined in Practices E716 and can also be applied to other types of samples provided that suitable reference materials are available. Also, other sample forms can be melted and cast into a disk, using an appropriate mold, as described in Practices E716. However, some elements (for example, magnesium) readily form oxides, while others (for example, sodium, lithium, calcium, and strontium) are volatile, and may be lost to varying degrees during the melting process.
language	English
title	Standard Test Method for Analysis of Aluminum and Aluminum Alloys by Spark Atomic Emission Spectrometry	en
title	ASTM E1251-24	num
type	standard
status	Active
tree	ASTM - ASTM International:;2024
contenttype	fulltext
scope	1.1 This test method describes the analysis of aluminum and its alloys by spark-atomic emission spectrometry (Spark-AES). The aluminum specimen to be analyzed may be in the form of a chill cast disk, casting, foil, sheet, plate, extrusion, or some other wrought form or shape. The elements covered in the scope of this method are listed as follows. Element Tested Mass Fraction Range (Wt %) Antimony 0.001 to 0.003 Arsenic 0.001 to 0.006 Beryllium 0.0004 to 0.24 Bismuth 0.03 to 0.6 Boron 0.0006 to 0.009 Calcium 0.0002 to 0.04 Chromium 0.001 to 0.23 Cobalt 0.4 to 1.60 Copper 0.001 to 5.5 Gallium 0.02 to 0.11 Iron 0.2 to 0.5 Lead 0.04 to 0.6 Lithium 0.0003 to 2.1 Magnesium 0.03 to 5.4 Manganese 0.001 to 1.2 Nickel 0.005 to 2.6 Phosphorus 0.003 to 0.017 Silicon 0.07 to 16 Sodium 0.003 to 0.02 Strontium 0.03 to 11.0 Tin 0.03 to 21.0 Titanium 0.001 to 0.12 Vanadium 0.002 to 0.022 Zinc 0.002 to 5.7 Zirconium 0.001 to 0.12 Note 1: The mass fraction ranges given in the scope were established through cooperative testing (ILS) of selected reference materials. The range shown for each element does not demonstrate the actual usable analytical range for that element. The usable analytical range may be extended higher or lower based on individual instrument capability, spectral characteristics of the specific element wavelength being used, and the availability of appropriate reference materials. Warning—Mercury (Hg) is intentionally not included in the scope. Analysis of Hg in aluminum by Spark-AES is not recommended. Accurate analysis of Hg using this technique is compromised by the presence of an intense iron interference. Inaccurate reporting of Hg due to these interference effects can jeopardize the current designation of aluminum production as a mercury-free process. To demonstrate compliance with legislated Hg content limits, use of an alternate method capable of analysis with a minimum reporting limit of 0.0001% or lower is recommended. Suitable techniques include but are not limited to GD-MS, XRF, cold vapor AA, and ICP-MS. 1.2 This test method is suitable primarily for the analysis of chill cast disks as defined in Practices E716. Other forms may be analyzed, provided that: (1) they are sufficiently massive to prevent undue heating, (2) they allow machining to provide a clean, flat surface, which creates a seal between the specimen and the spark stand, and (3) reference materials of a similar metallurgical condition and chemical composition are available. 1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use. Specific safety and health statements are given in Section 10. 1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.
identifier DOI	10.1520/E1251-24