Experimental Study of Causes and Repair of Cracking of 1 1/4Cr- 1/2Mo Steel Equipment
Organization:
API - American Petroleum Institute
Year: 1996
Abstract: A multitask experimental study was conducted to provide the petroleum industry with solutions to recurring incidents of cracking in the application of welded l¼Cr-l½Mo steel for hydrogen processing equipment. The principal objective was to develop recommendations for the elimination of cracking that occurred during fabrication or early in operating life, was associated with repairs or was found after ex- tended service exposure at elevated temperature.
Collections
:
Show full item record
| contributor author | API - American Petroleum Institute | |
| date accessioned | 2017-09-04T16:09:49Z | |
| date available | 2017-09-04T16:09:49Z | |
| date copyright | 05/01/1996 | |
| date issued | 1996 | |
| identifier other | SHURCAAAAAAAAAAA.pdf | |
| identifier uri | https://yse.yabesh.ir/std/handle/yse/73073 | |
| description abstract | A multitask experimental study was conducted to provide the petroleum industry with solutions to recurring incidents of cracking in the application of welded l¼Cr-l½Mo steel for hydrogen processing equipment. The principal objective was to develop recommendations for the elimination of cracking that occurred during fabrication or early in operating life, was associated with repairs or was found after ex- tended service exposure at elevated temperature. | |
| language | English | |
| title | API PUBL 938-A | num |
| title | Experimental Study of Causes and Repair of Cracking of 1 1/4Cr- 1/2Mo Steel Equipment | en |
| type | standard | |
| page | 222 | |
| status | Active | |
| tree | API - American Petroleum Institute:;1996 | |
| contenttype | fulltext |